Welding equipment advices: how to become a better welder and how to choose the top welding equipment. How do I choose what size Tig Welding Rod should I use for the job? For sheet metal up to 1/8” thick, don’t use a welding rod that is bigger than the thickness of metal you are welding…at least not much bigger. A good example…is using a 3/32 rod for welding .040 metal. That will just give you a fit. The amperage is low and the weld puddle needs to be small in order to prevent blowing a hole…and then when you dip the rod into the puddle, the rod is a big heat sink and sucks the heat right out of the puddle making it hard to maintain a consistent size bead. But Beginners should probably not be practicing on really thin metal. If you are a beginner you should be practicing on around 1/8 ” thick metal, and the bigger the rod, the easier it is to feed. For 1/8 ” metal, Use larger diameter rods (3/32” to 1/8”) So here is the rule….thin metal, use a thin rod Thick metal, use a thicker rod. This might seem like a no brainer, but I have answered a lot of questions like this about the rod melting before it gets to the puddle. If torch angle and arc length are right, its usually the rod size.
And another tip is use the old school type of collet body(not gas lens) and one size smaller cup than you would use for steel that still provides good shielding. A smaller old school (not gas lens) TIG cup confines the shielding gas envelope to the puddle so that arc energy is not wasted in the form of frosty cleaning action outside the weld. A lot of Old timers use the small cups, they just don’t know why. Pay attention next time you weld aluminum and use a small cup and then turn the shielding gas flow down to around 12-15 cfh with a #6 cup and see if things don’t quiet down a bit.
The arc is shaped like a cone, with the tip at the electrode and the base on the metal being welded. The closer the electrode is held to the metal, the smaller the base of the cone — but as you pull the electrode farther away, the base (and puddle) gets larger. If the puddle gets too large, gravity will simply pull it away from the base metal, leaving a hole. This is why thin-gauge metals are especially challenging for beginners. Perhaps the most important skill needed for TIG welding is moving the torch in a controlled manner, with steady forward movement, while keeping the gap between the tip of the electrode and the base metal consistently small — usually in the range of 1/8 inch to 3/16 inch. It requires a lot of practice to precisely control the arc length, keeping it as short as you can without allowing the electrode to touch the base metal or filler rod.
Searching for the best Plasma Cutters? We recommend Welding Supplies Direct & Associate company TWS Direct Ltd is an online distributor of a wide range of welding supplies, welding equipment and welding machines. We supply Plasma Cutters, MIG, TIG, ARC Welding Machines and support consumables to the UK, Ireland and Europe.
Following some simple tips can help you take your MIG welding operation to the next level and ensure you are as safe, efficient and professional as any other shop. Welding helmets, gloves, close-toed shoes and clothes that fully cover exposed skin are essential. Make sure you wear flame-resistant natural fibers such as denim and leather, and avoid synthetic materials that will melt when struck by spatter, potentially causing burns. Also, avoid wearing pants with cuffs or shirts with pockets, as these can catch sparks and lead to injuries.